Our site saves small pieces of text information (cookies) on your device in order to deliver better content and for statistical purposes. You can disable the usage of cookies by changing the settings of your browser. By browsing our site without changing the browser settings you grant us permission to store that information on your device.I agree, do not show this message again.
RENBAO WANG1,* , HUI ZHANG1, QIONG MA2, HAIHONG NIU2, JINZHANG XU2
- Department ElectronicInformation and Electrical Engineering, Hefei University, Hefei 230601, China
- School of Electrical Engineering and A utomationutomation, Hefei University of Technology, Hefei 230009, China
A new type of TiO2 nano SiO2 hybrid film was prepared by mixing TiO2 with the nano sized SiO2 powder. The size of CdSe quantum dots (QDs) was about 2.6nm The spin coating method wa was applied to prepare CdSe QDs sens itized the TiO2 nano SiO2 hybrid film for the quantum dots sensitized solar cells QDSSCs application. It is found that the introduction of SiO2 and the capped ligands show notable influence on the photovoltaic performance. The power conversion efficiency of 1.74% was achieved by using the TiO2 nano SiO2 hybrid film modified with MPA MPA-capped CdSe TiO2 nano SiO2/CdSe(MPA)) under the illumination of one sun (AM1.5, 100mW/cm 2.
CdSe quantum d ots, TiO2 nano SiO2 hybrid photoanode, Sensitized, Solar cells.
Submitted at: Feb. 3, 2019
Accepted at: Feb. 17, 2020
RENBAO WANG, HUI ZHANG, QIONG MA, HAIHONG NIU, JINZHANG XU, Improved performance of quantum dots sensitized solar cells: a TiO2-nano-SiO2 hybrid photoanode modified with CdSe, Journal of Optoelectronics and Advanced Materials Vol. 22, Iss. 1-2, pp. 29-36 (2020)
- Download Fulltext
- Downloads: 224 (from 153 distinct Internet Addresses ).