Our site saves small pieces of text information (cookies) on your device in order to deliver better content and for statistical purposes. You can disable the usage of cookies by changing the settings of your browser. By browsing our site without changing the browser settings you grant us permission to store that information on your device.I agree, do not show this message again.
H. KANBUR CAVUS1,* , R. SAHINGOZ1
- Department of Physics, Yozgat Bozok University, Yozgat, 66900, Turkey
In this study, for the production of flexible photoanodes, a binder-free TiO2 paste has been prepared. The photoelectrodes fabricated with this paste at low temperature have been achieved a very good contact compared to the results prepared by conventional high temperature procedures. These flexible photoanodes have been sensitized with Ruthenizer N719 dye at 24 hours and this flexible photoanode and Pt counter electrode have been combined. The characteristic values of Jsc, Voc, FF and conversion efficiency (ɲ) have been obtained 20.9 mA/cm2, 671 mV, 0.57, and 7.95 % respectively for the flexible dye sensitized solar cell (DSSC)..
Flexible DSSC, Binder-free TiO2 paste, Fill factor, Power conversion efficiency.
Submitted at: Sept. 8, 2020
Accepted at: Aug. 16, 2021
H. KANBUR CAVUS, R. SAHINGOZ, Preparation and investigation of binder-free TiO2 paste for low temperature flexible DSSC applications, Journal of Optoelectronics and Advanced Materials Vol. 23, Iss. 7-8, pp. 359-365 (2021)
- Download Fulltext
- Downloads: 31 (from 25 distinct Internet Addresses ).