Our site saves small pieces of text information (cookies) on your device in order to deliver better content and for statistical purposes. You can disable the usage of cookies by changing the settings of your browser. By browsing our site without changing the browser settings you grant us permission to store that information on your device.
I agree, do not show this message again.Preparation of cobalt hydroxide and cobalt oxide nanostructures using ultrasonic waves and investigation of their optical and structural properties
R. SHOKRANI-HAVIGH1, Y. AZIZIAN-KALANDARAGH1,2,*
Affiliation
- Department of Physics, University of Mohaghegh Ardabili, P.O. Box 179, Ardabil, Iran
- Department of Engineering Sciences, Sabalan University of Advanced Technologies (SUAT), Namin, Iran
Abstract
Nanocrystalline cobalt hydroxide and cobalt oxide compounds have been prepared using ultrasound-assisted method and some of their optical and structural properties have been characterized by thermogravimetric analyses(TGA), X-ray diffraction (XRD), scanning electron microscope (SEM), and UV-Visible spectroscopy. The results of thermogravimetric analyses show a sharp change in TGA peak, and the oneset of the peak (at 250˚C) is transition temperature from hydroxide to oxide of the product. The optical absorption studies show that there are two direct band gaps in Co3O4 nanostructures. The XRD patterns of the prepared samples shows formation of pure cobalt oxide in cubic structure and cobalt hydroxide compound in hexagonal structure with average grain sizes are below 30 nm. Surface morphology of the prepared structures shows that the nanoparticles from nearly globular aggregates of microdimensions..
Keywords
Cobalt oxide, Cobalt hydroxide, X-ray diffraction, Optical properties, Scanning electron microscopy (SEM).
Submitted at: July 4, 2014
Accepted at: April 6, 2017
Citation
R. SHOKRANI-HAVIGH, Y. AZIZIAN-KALANDARAGH, Preparation of cobalt hydroxide and cobalt oxide nanostructures using ultrasonic waves and investigation of their optical and structural properties, Journal of Optoelectronics and Advanced Materials Vol. 19, Iss. 3-4, pp. 283-288 (2017)
- Download Fulltext
- Downloads: 2202 (from 1302 distinct Internet Addresses ).