Our site saves small pieces of text information (cookies) on your device in order to deliver better content and for statistical purposes. You can disable the usage of cookies by changing the settings of your browser. By browsing our site without changing the browser settings you grant us permission to store that information on your device.

I agree, do not show this message again.

Rapid surface modification of EPDM with oxygen and nitrogen plasmas: a comparative study

J. H. MORAES1,* , H. S. MACIEL1, J. C. N. DUTRA2, S. A. C. MELLO2, A. S. DA SILVA SOBRINHO1, M. MASSI1

Affiliation

  1. LPP, Technological Institute of Aeronautics, CTA, Pça Mal Eduardo Gomes 50, 12228-900 São José dos Campos – S.P., Brazil
  2. AQI, Institute of Aeronautics and Space, CTA, Pça Mal Eduardo Gomes 50, 12228-904, São José dos Campos – S.P., Brazil

Abstract

This work presents the adhesion properties of plasma treated EPDM (ethylene propylene diene monomer) vulcanized rubber used in missile and rocket manufacturing. The EPDM rubber surface was treated in a RIE (reactive ion etching) plasma reactor using two different gas mixtures, oxygen/argon and nitrogen/argon. Contact angle measurements were used to obtain the dispersive and polar components of the surface tension of the treated samples, and FT-IR was used to characterize the surface. Both plasma treatments promote an enhancement of the adhesive properties of the EPDM rubber. However, the improvement factor depends on the gas mixture used. For treatment with an oxygen/argon mixture, functional groups such as C-O, C=O, O-C=O, C-O-O and CO3 are formed in the rubber surface. In the case of a nitrogen/argon mixture, the functional groups formed on the surface are C-N, C=N and C≡N, beyond the functional groups C-O, due to the rubber oxidation. Therefore, the higher polarity of nitrogen containing groups makes the treatment with the nitrogen/argon mixture more efficient..

Keywords

Surface activation, r.f. plasma, Rubber.