Our site saves small pieces of text information (cookies) on your device in order to deliver better content and for statistical purposes. You can disable the usage of cookies by changing the settings of your browser. By browsing our site without changing the browser settings you grant us permission to store that information on your device.I agree, do not show this message again.
S. KAYRAL1, R. TÜLEK1, S. GÖKDEN1,* , A. TEKE1
- Department of Physics, Faculty of Science and Letter, Balıkesir University, Çağış Kampüsü, 10145 Balıkesir, Turkey
Temperature and excitation power density dependent photoluminescence (PL) studies were performed on Ga-doped ZnO (GZO) thin films grown on a-(112 ̅0) and c-(0001) sapphire substrates by Molecular Beam Epitaxy (MBE). The observed PL spectra are dominated by excitonic as well as defect related transitions. The origins of the emission bands were determined by applying the Gaussian fit to 10K PL spectra and discussed and compared with those available in literature. The shape of the temperature dependence of the PL spectra did show any discernable dependence on the substrate orientation used. The peak energies of excitonic transitions redshifted with increasing temperature with a total shift of about 70 meV (from 10K to 300 K). From the temperature activation energies of 6 and 40 meV were obtained from a bi-exponential empirical equation fitting. The excitation power density dependence of total integrated PL intensities and the ratio of peak intensities of the excitonic transition to yellow luminescence revealed that they follow a power law in the form of I_T or I_ex⁄I_YL ∝P_E^k, where P_E is the excitation power density and k is the power factor..
Ga-doped ZnO (GZO), Photoluminescence (PL), Exitonic transitions, Optical properties.
Submitted at: Oct. 19, 2021
Accepted at: Oct. 5, 2022
S. KAYRAL, R. TÜLEK, S. GÖKDEN, A. TEKE, The temperature and excitation power density dependent photoluminescence study of Ga-doped ZnO thin films, Journal of Optoelectronics and Advanced Materials Vol. 24, Iss. 9-10, pp. 471-476 (2022)
- Download Fulltext
- Downloads: 1 (from 1 distinct Internet Addresses ).